Catalyst for conversion of hydrocarbons, process of making and process of using thereof

ABSTRACT

This invention is for a catalyst for conversion of hydrocarbons. The catalyst contains a zeolite with one element from Group 13, Group 14, or the first series transition metals and, optionally, germanium and/or aluminum in the zeolite framework. At least one Group 10 metal, such as platinum, is deposited on the zeolite. Examples of the elements in the framework are tin, boron, iron or titanium. The catalyst is prepared by synthesizing a zeolite with one element from Group 13, Group 14, or the first series transition metals and, optionally, germanium and/or aluminum in the zeolite framework; depositing the metal; and calcining after preparation of the zeolite and before or after depositing the metal. The catalyst may be used in a process for the conversion of hydrocarbons, such as propane to aromatics, by contacting the catalyst with alkanes having 2 to 12 carbon atoms per molecule and recovering the product.

CROSS REFERENCE TO RELATED APPLICATIONS

This application is a continuation of U.S. patent application Ser. No. 12/125,753, filed May 22, 2008, which claims the benefit of U.S. Provisional Application Ser. No. 60/931,610, filed May 24, 2007, both of which are incorporated herein by reference, in their entirety.

BACKGROUND OF THE INVENTION

1. Field of the Invention

This invention relates to a catalyst for hydrocarbon conversion, e.g., a catalyst for the aromatization of alkanes, olefins and mixtures thereof having two to twelve carbon atoms per molecule. The catalyst is a microporous silicate, aluminosilicate, aluminophosphate or silicoaluminophosphate on which a metal has been deposited.

2. Description of the Prior Art

Crystalline silicates, aluminosilicates, aluminophosphates and silicoaluminophosphates are known catalysts for hydrocarbon conversion and may contain other metals. An aluminosilicate such as a zeolite may include not only aluminum and silicon but other trivalent elements which replace aluminum and other tetravalent elements which replace silicon. Also, other elements may be deposited on the silicate, aluminosilicate, aluminophosphate or silicoaluminophosphate.

U.S. Pat. No. 4,310,440 discloses crystalline aluminophosphates having a framework structure with chemical composition in mole ratios of 1 Al₂O₃:1.0±0.2 P₂O₅ and being microporous with uniform pores of nominal diameters from about 3 to about 10 angstroms.

U.S. Pat. No. 4,440,871 discloses crystalline microporous silicoaluminophosphates having pores which are uniform and have nominal diameters of greater than about 3 angstroms with a chemical composition of mole fractions of silicon, aluminum and phosphorus within the pentagonal composition area defined by

Mole Fraction x y z A 0.01 0.47 0.52 B 0.94 0.01 0.05 C 0.98 0.01 0.01 D 0.39 0.60 0.01 E 0.01 0.60 0.39 where x, y and z are the mole fractions of silicon, aluminum and phosphorus and ACBDE are points defining a pentagonal area of a ternary diagram as shown in FIG. 1 of U.S. Pat. No. 4,440,871.

SUMMARY OF THE INVENTION

This invention provides a catalyst containing silicon, aluminum, phosphorus, as needed to form a silicate, aluminosilicate, aluminophosphate (AlPO) or silicoaluminophosphate (SAPO) with at least one other element selected from Group 4, Group 5, Group 13, Group 14, Group 15 and the first series transition metals in a three dimensional interconnecting crystalline tetrahedral framework. The crystalline tetrahedral framework is synthesized from an aqueous gel containing, as needed, a silica source, an aluminum source, a phosphorus source, a source for the Group 4, Group 5, Group 13, Group 14, Group 15 and the first series transition metal element(s) and, optionally, an organic structure-directing agent. The reaction mixture is heated to form crystals and then cooled. The crystals are separated from the synthesis liquor and are washed, dried and calcined. At least one metal selected from Group 6, Group 7, Group 8, Group 9 or Group 10 is deposited on the silicate, aluminosilicate, aluminophosphate or silicoaluminophosphate (hereinafter referred to as “deposited metal”). The catalyst may be used in a process for converting C₂-C₁₂ hydrocarbons into aromatics.

One example of the invention is a catalyst on which at least one Group 10 metal, such as platinum, is deposited on a zeolite having incorporated into the zeolite framework one element selected from the group consisting of Group 13, Group 14, and the first series transition metal element(s) and, optionally, at least one element selected from the group consisting of germanium and aluminum. This example includes a process for synthesizing a zeolite by: a) preparing a zeolite having incorporated into the zeolite framework one element selected from the group consisting of Group 13, Group 14, and the first series transition metal element(s) and, optionally, at least one element selected from the group consisting of germanium and aluminum; b) depositing at least one metal selected from Group 10 on the zeolite; and c) calcining the zeolite, said calcining occurring after preparation of the zeolite, before depositing at least one metal selected from Group 10 on the zeolite or after depositing at least one metal selected from Group 10 on the zeolite. This example of the invention also includes a process for the conversion of hydrocarbons of: a) contacting a hydrocarbon stream containing alkanes, olefins and mixtures thereof having 2 to 12 carbon atoms per molecule with at least one zeolite-based catalyst wherein the zeolite having incorporated into the zeolite framework one element selected from the group consisting of Group 13, Group 14, and the first series transition metal element(s) and, optionally, at least one element selected from the group consisting of germanium and aluminum and wherein at least one metal selected from Group 10 has been deposited on the zeolite; and b) recovering the product.

BRIEF DESCRIPTION OF THE DRAWINGS

A more complete appreciation of the invention and many of the attendant advantages thereof will be readily understood by reference to the following detailed description when considered in connection with the accompanying drawings wherein:

FIG. 1 is a graph of propane conversion, BTX selectivity and fuel gas selectivity for Pt/GeSnAl-ZSM-5

FIG. 2 is a graph of propane conversion, BTX selectivity and fuel gas selectivity for Pt/Sn-ZSM-5

FIG. 3 is a graph of propane conversion, BTX selectivity and fuel gas selectivity for Pt/SnAl-ZSM-5

FIG. 4 is a graph of propane conversion, BTX selectivity and fuel gas selectivity for Pt/B-ZSM-5

FIG. 5 is a graph of propane conversion, BTX selectivity and fuel gas selectivity for Pt/BAl-ZSM-5

FIG. 6 is a graph of propane conversion, BTX selectivity and fuel gas selectivity for Pt/FeAl-ZSM-5

FIG. 7 is a graph of propane conversion, BTX selectivity and fuel gas selectivity for Pt/TiAl-ZSM-5

DETAILED DESCRIPTION OF THE INVENTION

Crystalline silicates, aluminosilicates, aluminophosphates and silicoaluminophosphates have uniform pores through which molecules can diffuse. Aluminosilicates include zeolites. Examples of zeolites are MFI (ZSM-5), BEA (Beta), MWW (MCM-22), MOR (Mordenite), LTL (Zeolite L), MTT (ZSM-23), MTW (ZSM-12), TON (ZSM-22) and MEL (ZSM-11).

Crystalline silicates, aluminosilicates, aluminophosphates and silicoaluminophosphates have structures of TO₄ tetrahedra, which form a three dimensional network by sharing oxygen atoms where T represents tetravalent elements, such as silicon; trivalent elements, such as aluminum; and pentavalent elements, such as phosphorus.

“Zeolite” in the present application includes aluminosilicates with open three-dimensional framework structures composed of corner-sharing TO₄ tetrahedra, where T is Al or Si, but also includes tetravalent, trivalent and divalent T atoms which able to isoelectronically replace Si and Al in the framework, e.g., germanium (4+), titanium (4+), boron (3+), gallium (3+), iron (3+), zinc (2+) and beryllium (2+). “Zeolite” is primarily a description of structure, not composition.

Silicates, aluminosilicates, aluminophosphates and silicoaluminophosphates generally crystallize from an aqueous solution. The typical technique for synthesizing silicates, aluminosilicates, aluminophosphates or silicoaluminophosphates comprises converting an aqueous gel of a silica source, an aluminum source and a phosphorus source, as needed, to crystals by a hydrothermal process, employing a dissolution/recrystallization mechanism. The reaction medium may also contain an organic structure-directing agent which is incorporated in the microporous space of the crystalline network during crystallization, thus controlling the construction of the network and assisting to stabilize the structure through the interactions with the silicon, aluminum or phosphorus components.

The aqueous gel contains in addition to the silica source, the aluminum source, the phosphorus source, as needed, and the optional organic structure-directing agent, and a source of at least one other element from Group 4, Group 5, Group 13, Group 14, Group 15 or the first series transition metals to be incorporated into the framework of the silicate, aluminosilicate, aluminophosphate or silicoaluminophosphate.

Examples of the silica source are silicon oxide or silica (SiO₂) which is available in various forms, such as silica sol, commercially available as Ludox AS-40™, precipitated silica, commercially available as Ultrasil VN3SP™ and fumed silica, commercially available as Aerosil 200™.

Examples of the aluminum source are sodium aluminate, aluminum nitrate, aluminum sulfate, aluminum hydroxide and pseudobohemite.

Examples of the phosphorus source are phosphoric acid (85 wt %), P₂O₅, orthophosphoric acid, triethylphosphate and sodium metaphosphate.

Examples of the source of Group 4, Group 5, Group 13, Group 14, Group 15 and the first series transition metals are oxides, chlorides, sulfates, alkoxides, fluorides, nitrates and oxalates.

Examples of the structure-directing agent are organic amine and quaternary ammonium compounds and salts and cations thereof, such as tetra n-propyl ammonium hydroxide, tetra n-propyl ammonium bromide and tetra n-propyl ammonium chloride, tetraethyl ammonium hydroxide, hexamethyleneimine, 1,4-di(1′4′-diazabicyclo[2.2.2]octane)butane hydroxide, morpholine, cyclohexylamine and diethylethanolamine, N,N′-diisopropyl imidazolium cation, tetrabutylammonium compounds, di-n-propylamine (DPA), tripropylamine, triethylamine (TEA), triethanolamine, piperidine, 2-methylpyridine, N,N-dimethylbenzylamine, N,N-diethylethanolamine, dicyclohexylamine, N,N-dimethylethanolamine, choline cation, N,N′-dimethylpiperazine, 1,4-diazabicyclo(2,2,2)octane, N′,N′,N,N-tetramethyl-(1,6)hexanediamine, N-methyldiethanolamine, N-methyl-ethanolamine, N-methyl piperidine, 3-methyl-piperidine, N-methylcyclohexylamine, 3-methylpyridine, 4-methyl-pyridine, quinuclidine, N,N′-dimethyl-1,4-diazabicyclo(2,2,2) octane ion; di-n-butylamine, neopentylamine, di-n-pentylamine, isopropylamine, t-butyl-amine, ethylenediamine, pyrrolidine, 2-imidazolidone, a N-benzyl-1,4-diazabicyclo[2.2.2]octane cation, a 1-[1-(4-chlorophenyl)-cyclopropylmethyl]-1-ethyl-pyrrolidinium or 1-ethyl-1-(1-phenyl-cyclopropylmethyl)-pyrrolidium cation and mixtures thereof.

The reaction may also utilize an acid as a reagent. The acid may be a Bronsted acid or a Lewis acid. Examples without limitation of an acid useful in the present invention are sulfuric acid, acetic acid, nitric acid, phosphoric acid, hydrochloric acid, hydrofluoric acid, oxalic acid or formic acid.

The reaction mixture is stirred and heated to a temperature of about 100° C. to about 200° C. to form crystals. The reaction mixture is cooled to room temperature. The crystals are separated from the synthesis liquor. The liquid portion of the synthesis liquor may be removed by filtration, evaporation, spray drying or any other means for removing liquid, e.g., water, from the crystals. The crystals are washed with water and then dried and calcined.

The silicates are essentially aluminum-free but may contain aluminum and other impurities up to 500 ppm.

The aluminosilicates may have a silicon to aluminum atomic ratio (Si:Al) greater than 2:1. In one embodiment of the present invention, the silicon to aluminum atomic ratio is in the range from 15:1 to 200:1. In another embodiment of the present invention, the silicon to aluminum atomic ratio is in the range from 18:1 to 100:1.

The aluminophosphates may have an aluminum to phosphorus atomic ratio (Al:P) in the range from about 0.8:1 to about 1.2:1 as disclosed in U.S. Pat. No. 4,310,440, hereby incorporated by reference.

The silicoaluminophosphates may have a silicon to aluminum to phosphorus atomic ratio represented by (S_(x)Al_(y)P_(z))O₂ where “x”, “y” and “z” represent the mole fractions of silicon, aluminum and phosphorus respectively, present as tetrahedral oxides, said mole fractions being such that they are within the pentagonal compositional area defined by points ABCD and E of a ternary diagram with values represented in the table below:

Mole Fraction x y z A 0.01 0.47 0.52 B 0.94 0.01 0.05 C 0.98 0.01 0.01 D 0.39 0.60 0.01 E 0.01 0.60 0.39 as disclosed in U.S. Pat. No. 4,440,871, hereby incorporated by reference.

The amount of Group 4, Group 5, Group 13, Group 14, Group 15 and the first series transition metals present in the crystalline framework is in the range from 0.1 wt. % to 25 wt. %. In one embodiment of the present invention, this range is from 0.1 wt. % to 10 wt. %. In another embodiment of the present invention, this range is from 0.1 wt. % to 5 wt. %.

The silicate, aluminosilicate, aluminophosphate or silicoaluminophosphate has average pore size in the range from 2 angstroms to 20 angstroms, i.e., microporous.

At least one metal selected from Group 6, Group 7, Group 8, Group 9 or Group 10 is deposited on the silicate, aluminosilicate, aluminophosphate or silicoaluminophosphate (“deposited metal”). The metal is deposited not only on the surface of the silicate, aluminosilicate, aluminophosphate or silicoaluminophosphate but also in the pores and channels which occur in the silicate, aluminosilicate, aluminophosphate or silicoaluminophosphate. The metal is deposited on the silicate, aluminosilicate, aluminophosphate or silicoaluminophosphate by any known method of depositing a metal on a silicate, aluminosilicate, aluminophosphate or silicoaluminophosphate. Typical methods of depositing a metal on a silicate, aluminosilicate, aluminophosphate or silicoaluminophosphate are ion exchange, impregnation and vapor deposition. In one embodiment of the present invention, the metal is present in the range from 0.05% to 3% by weight. In another embodiment of the present invention, the metal is present in the range from 0.1% to 2% by weight. In another embodiment of the present invention, the metal is present in the range from 0.2 to 1.5% by weight.

However, for silicate, aluminosilicate, aluminophosphate or silicoaluminophosphate-based catalysts on which metals have been deposited, the process temperatures and catalyst regeneration temperatures cause the metal to “sinter”, i.e., agglomeration of the metal particles resulting in an increase of metal particle size on the surface of the zeolite and a decrease of metal surface area, causing a loss of catalyst performance, specifically catalyst performance, e.g., activity and/or selectivity.

Without the present invention and its claims being limited by theory, it is believed that certain elements in the framework and certain metals deposited on the silicate, aluminosilicate, aluminophosphate or silicoaluminophosphate associate to resist sintering of the deposited metal. U.S. Pat. No. 6,784,333 discloses and claims an aluminum-silicon-germanium zeolite on which platinum has been deposited for use in a process for the aromatization of hydrocarbons. The presence of germanium in the framework of the zeolite and the presence of platinum deposited on the zeolite apparently results in higher selectivity for benzene, toluene and xylenes (BTX) which remains essentially constant over a significant time on stream. Without the invention of U.S. Pat. No. 6,784,333 and its claims being limited by theory, it may be that the germanium in the framework and the platinum deposited on the zeolite associate such that the platinum remains dispersed and sintering is reduced.

Besides germanium, there may be other elements in the crystalline framework which associate with platinum or other deposited metals. Elements in the crystalline framework may be selected from Group 4, Group 5, Group 13, Group 14, Group 15 and the first series transition metals of the Periodic Table of Elements. Specific examples of these elements are germanium, boron, gallium, indium, tin, titanium, zirconium, vanadium, chromium, iron, niobium and phosphorus. One or more elements may be in the crystalline framework. Specific examples of elements in the framework are germanium and at least one element selected from the group consisting of tin and boron.

Besides platinum, there may be other deposited metals which associate with germanium or other elements in the crystalline framework. Deposited metals may be selected from Group 6, Group 7, Group 8, Group 9 and Group 10 of the Periodic Table of Elements. Specific examples of the deposited metal are platinum, molybdenum, rhenium, nickel, ruthenium, rhodium, palladium, osmium and iridium. One or more metals, such as bimetallics, e.g., Pt/Sn, Pt/Ge, Pt/Pb or metal/metal oxide combinations, e.g. Pt/GeO₂, may be deposited.

The crystalline framework of which these elements from Group 4, Group 5, Group 13, Group 14, Group 15 and the first series transition metals are part and on which metals selected from Group 6, Group 7, Group 8, Group 9 and Group 10 are deposited need not be limited to a zeolite but may be any microporous silicate, aluminosilicate, aluminophosphate or silicoaluminophosphate.

Before or after deposition of the metal, the silicate, aluminosilicate, aluminophosphate or silicoaluminophosphate may be bound by oxides or phosphates of magnesium, aluminum, titanium, zirconium, thorium, silicon, boron or mixtures thereof. The process steps of binding and depositing metal can occur in any order. Binding may occur before or after metal deposition.

The catalyst may be calcined at different stages in the synthesis. For example, there may be a first calcination of the silicate, aluminosilicate, aluminophosphate or silicoaluminophosphate to remove the organic structure-directing agent followed by metal deposition and subsequent calcinations at lower temperatures. The calcination to remove the organic structure-directing agent is at a temperature of about 300° C. to about 1000° C. or about 300° C. to about 750° C. for a time sufficient to remove essentially all of any structure-directing agent, e.g., one to six hours or about four hours. One example of calcination is at 550° C. for ten hours. Calcination may occur after binding. This calcination is at a temperature in the range of from about 300° C. to about 1000° C. for a time in the range of from about one hour to about 24 hours. Calcination may also occur after metal deposition to fix the metal. This calcination should not exceed a temperature of 500° C. and may be at a temperature of about 200° C. to about 500° C. for a time in the range of from about 0.5 hour to about 24 hours. These calcinations need not be separate but may be combined to accomplish more than one purpose. When the silicate, aluminosilicate, aluminophosphate or silicoaluminophosphate is calcined, it may be bound or unbound and it may have metal deposited on it or not. Calcination can occur in an environment of oxygen, nitrogen, hydrogen, water vapor, helium and mixtures thereof.

The catalyst, bound and unbound, will have porosity in addition to the uniform porosity of the silicate, aluminosilicate, aluminophosphate or silicoaluminophosphate. For an unbound catalyst, the average pore size of the catalyst can vary for bound and unbound catalyst and is in the range from 2 angstroms to 100 angstroms. In one embodiment of the present invention, the average pore size is in the range from 5 angstroms to 50 angstroms. In another embodiment of the present invention, the average pore size is in the microporous range from 5 angstroms to 20 angstroms. For a bound catalyst, the average pore size of the catalyst may vary from 5 angstroms up to 100 microns.

Some catalysts used for hydrocarbon conversion are susceptible to sulfur poisoning. However, for some catalysts used for hydrocarbon conversion, modest amounts of sulfur, such as about 0 to 200 ppm in the feed, are acceptable and sometimes preferred. The catalyst may also be pretreated with sulfur. A standard sulfurization method that is well known in the art consists in heating in the presence of a sulfur compound, such as hydrogen sulfide, or a mixture of a sulfur compound and an inert gas, such as hydrogen or nitrogen, to a temperature of between 150 and 800° C. Non-limiting examples of sulfur compounds are H₂S, an organosulfide compound, such as dimethyl disulfide or DMSO (dimethyl sulfoxide), or C_(n)H_(2n+2)S or C_(n)H_(2n+2)S₂, where n=1-20. In one embodiment of the present invention, the temperature is between 250 and 600° C.

The catalyst may contain a reaction product, such as a sulfide of the deposited metal, that is formed by contacting the catalyst with sulfur or a sulfur compound. In one embodiment of the present invention, the amount of sulfur on the catalyst is in the range of from 10 ppm to 0.1 wt. %.

The catalyst may also contain elements other than sulfur, such as tin, germanium or lead. These elements would be present in the range of from 1:1 to 1:100 as a ratio of the deposited metal to tin, germanium or lead. These elements may be added to the catalyst by wet impregnation, chemical vapor deposition or other methods known in the art.

The silicate, aluminosilicate, aluminophosphate or silicoaluminophosphate-based catalyst which contains at least one element selected from Group 4, Group 5, Group 13, Group 14, Group 15 and the first series transition metals isomorphously incorporated into the zeolite framework and at least one metal selected from Group 6, Group 7, Group 8, Group 9 and Group 10 deposited on the zeolite can be used in a process for conversion of hydrocarbon streams containing C₂-C₁₂ alkanes, olefins and mixtures thereof which may be straight, branched, cyclic or mixtures thereof, into aromatics.

The zeolite may be base-exchanged with an alkali metal or alkaline earth metal, such as cesium, potassium, sodium, rubidium, barium, calcium, magnesium and mixtures thereof, to reduce acidity and form a non-acidic zeolite. A non-acidic zeolite has substantially all of its cationic sites of exchange, e.g., those typically associated with aluminum, occupied by nonhydrogen cationic species, e.g., alkali or alkaline earth metals. These cationic sites are often responsible for cracking of hydrocarbons into undesired products. A zeolite may be non-acidic by exchange with a base or by having a low aluminum content. The base-exchange may occur before or after the noble metal is deposited. Such a base-exchanged catalyst may be used to convert C₆-C₁₂ alkanes, such as might be obtained from natural gas condensate, light naphtha, raffinate from aromatics extraction and other refinery or chemical processes, to aromatics, such as benzene, ethyl benzene, toluene and xylenes. Base-exchange may take place during synthesis of the zeolite with an alkali metal or alkaline earth metal being added as a component of the reaction mixture or may take place with a crystalline zeolite before or after deposition of the noble metal. The zeolite is base-exchanged to the extent that most or all of the cations associated with aluminum are alkali metal or alkaline earth metal. An example of a monovalent base:aluminum molar ratio in the zeolite after base exchange is at least about 0.9. For a divalent or trivalent base, the molar ratio would be half (0.45) or a third (0.3) as that for a monovalent base, respectively, and for mixtures of monovalent, divalent and trivalent bases, the above molar ratios would be apportioned by their respective content in the mixture.

Depending on the element incorporated into the zeolite framework, the zeolite may be non-acidic, within the meaning and for the purposes of the present invention, without base-exchange, e.g., boron, germanium or tin in an aluminum-free zeolite. “Aluminum-free” has a meaning of having aluminum content of no more than 0.4 wt %.

Examples of hydrocarbon conversion processes for which this catalyst can be used are:

-   -   (A) The catalytic cracking of a naphtha feed to produce light         olefins. Typical reaction conditions include from about 500° C.         to about 750° C., pressures of subatmospheric or atmospheric,         generally ranging up to about 10 atmospheres (gauge) and         catalyst residence time (volume of the catalyst/feed rate) from         about 10 milliseconds to about 10 seconds.     -   (B) The catalytic cracking of high molecular weight hydrocarbons         to lower weight hydrocarbons. Typical reaction conditions for         catalytic cracking include temperatures of from about 400° C. to         about 700° C., pressures of from about 0.1 atmosphere (bar) to         about 30 atmospheres, and weight hourly space velocities of from         about 0.1 to about 100 hr⁻¹.     -   (C) The transalkylation of aromatic hydrocarbons in the presence         of polyalkylaromatic hydrocarbons. Typical reaction conditions         include a temperature of from about 200° C. to about 500° C., a         pressure of from about atmospheric to about 200 atmospheres, a         weight hourly space velocity of from about 1 to about 100 hr⁻¹         and an aromatic hydrocarbon/polyalkylaromatic hydrocarbon mole         ratio of from about 1/1 to about 16/1.     -   (D) The isomerization of aromatic (e.g., xylene) feedstock         components. Typical reaction conditions for such include a         temperature of from about 230° C. to about 510° C., a pressure         of from about 0.5 atmospheres to about 50 atmospheres, a weight         hourly space velocity of from about 0.1 to about 200 hr⁻¹ and a         hydrogen/hydrocarbon mole ratio of from about 0 to about 100.     -   (E) The dewaxing of hydrocarbons by selectively removing         straight chain paraffins. The reaction conditions are dependent         in large measure on the feed used and upon the desired pour         point. Typical reaction conditions include a temperature between         about 200° C. and 450° C., a pressure up to 3,000 psig and a         liquid hourly space velocity from 0.1 to 20 hr⁻¹.     -   (F) The alkylation of aromatic hydrocarbons, e.g., benzene and         alkylbenzenes, in the presence of an alkylating agent, e.g.,         olefins, formaldehyde, alkyl halides and alcohols having 1 to         about 20 carbon atoms. Typical reaction conditions include a         temperature of from about 100° C. to about 500° C., a pressure         of from about atmospheric to about 200 atmospheres, a weight         hourly space velocity of from about 1 hr⁻¹ to about 100 hr⁻¹ and         an aromatic hydrocarbon/alkylating agent mole ratio of from         about 1/11 to about 20/1.     -   (G) The alkylation of aromatic hydrocarbons, e.g., benzene, with         long chain olefins, e.g., C₁₄ olefin. Typical reaction         conditions include a temperature of from about 50° C. to about         200° C., a pressure of from about atmospheric to about 200         atmospheres, a weight hourly space velocity of from about 2 hr⁻¹         to about 2000 hr⁻¹ and an aromatic hydrocarbon/olefin mole ratio         of from about 1/1 to about 20/1. The resulting products from the         reaction are long chain alkyl aromatics which when subsequently         sulfonated have particular application as synthetic detergents.     -   (H) The alkylation of aromatic hydrocarbons with light olefins         to provide short chain alkyl aromatic compounds, e.g., the         alkylation of benzene with propylene to provide cumene. Typical         reaction conditions include a temperature of from about 10° C.         to about 200° C., a pressure of from about 1 to about 30         atmospheres, and an aromatic hydrocarbon weight hourly space         velocity (WHSV) of from 1 hr⁻¹ to about 50 hr⁻¹.     -   (I) The hydrocracking of heavy petroleum feedstocks, cyclic         stocks, and other hydrocrack charge stocks. The zeolite-bound         high silica zeolite will contain an effective amount of at least         one hydrogenation component of the type employed in         hydrocracking catalysts.     -   (J) The alkylation of a reformate containing substantial         quantities of benzene and toluene with fuel gas containing short         chain olefins (e.g., ethylene and propylene) to produce mono-         and dialkylates. Preferred reaction conditions include         temperatures from about 100° C. to about 250° C., a pressure of         from about 100 to about 800 psig, a WHSV-olefin from about 0.4         hr⁻¹ to about 0.8 hr⁻¹, a WHSV-reformate of from about 1 hr⁻¹ to         about 2 hr⁻¹ and, optionally, a gas recycle from about 1.5 to         2.5 vol/vol fuel gas feed.     -   (K) The alkylation of aromatic hydrocarbons, e.g., benzene,         toluene, xylene, and naphthalene, with long chain olefins, e.g.,         C₁₄ olefin, to produce alkylated aromatic lube base stocks.         Typical reaction conditions include temperatures from about         100° C. to about 400° C. and pressures from about 50 to 450         psig.     -   (L) The alkylation of phenols with olefins or equivalent         alcohols to provide long chain alkyl phenols. Typical reaction         conditions include temperatures from about 100° C. to about 250°         C., pressures from about 1 to 300 psig and total WHSV of from         about 2 hr⁻¹ to about 10 hr⁻¹.     -   (M) The conversion of light paraffins to olefins and/or         aromatics. Typical reaction conditions include temperatures from         about 425° C. to about 760° C. and pressures from about 10 to         about 2000 psig.     -   (N) The conversion of light olefins to gasoline, distillate and         lube range hydrocarbons. Typical reaction conditions include         temperatures of from about 175° C. to about 500° C. and a         pressure of from about 10 to about 2000 psig.     -   (O) Two-stage hydrocracking for upgrading hydrocarbon streams         having initial boiling points above about 200° C. to premium         distillate and gasoline boiling range products or as feed to         further fuels or chemicals processing steps. The first stage can         be the zeolite-bound high silica zeolite comprising one or more         catalytically active substances, e.g., a Group 8 metal, and the         effluent from the first stage would be reacted in a second stage         using a second zeolite, e.g., zeolite Beta, comprising one or         more catalytically active substances, e.g., a Group 8 metal, as         the catalyst. Typical reaction conditions include temperatures         from about 315° C. to about 455° C., a pressure from about 400         to about 2500 psig, hydrogen circulation of from about 1000 to         about 10,000 SCF/bbl and a liquid hourly space velocity (LHSV)         of from about 0.1 to 10 hr⁻¹.     -   (P) A combination hydrocracking/dewaxing process in the presence         of the zeolite-bound high silica zeolite comprising a         hydrogenation component and a zeolite such as zeolite Beta.         Typical reaction conditions include temperatures from about         350° C. to about 400° C., pressures from about 1400 to about         1500 psig, LHSV from about 0.4 to about 0.6 hr⁻¹ and a hydrogen         circulation from about 3000 to about 5000 SCF/bbl.     -   (Q) The reaction of alcohols with olefins to provide mixed         ethers, e.g., the reaction of methanol with isobutene and/or         isopentene to provide methyl-t-butyl ether (MTBE) and/or t-amyl         methyl ether (TAME). Typical conversion conditions include         temperatures from about 20° C. to about 200° C., pressures from         2 to about 200 atm, WHSV (gram-olefin per hour gram-zeolite)         from about 0.1 hr⁻¹ to about 200 hr⁻¹ and an alcohol to olefin         molar feed ratio from about 0.1/1 to about 5/1.     -   (R) The disproportionation of aromatics, e.g. the         disproportionation of toluene to make benzene and xylenes.         Typical reaction conditions include a temperature of from about         200° C. to about 760° C., a pressure of from about atmospheric         to about 60 atmosphere (bar), and a WHSV of from about 0.1 hr⁻¹         to about 30 hr⁻¹.     -   (S) The conversion of naphtha (e.g., C₆-C₁₀) and similar         mixtures to highly aromatic mixtures. Thus, normal and slightly         branched chained hydrocarbons, preferably having a boiling range         above about 40° C., and less than about 200° C., can be         converted to products having a substantially higher octane         aromatics content by contacting the hydrocarbon feed with the         zeolite at a temperature in the range of from about 400° C. to         600° C., preferably 480° C. to 550° C. at pressures ranging from         atmospheric to 40 bar, and liquid hourly space velocities (LHSV)         ranging from 0.1 to 15 hr⁻¹.     -   (T) The adsorption of alkyl aromatic compounds for the purpose         of separating various isomers of the compounds.     -   (U) The conversion of oxygenates, e.g., alcohols, such as         methanol, or ethers, such as dimethylether, or mixtures thereof         to hydrocarbons including olefins and aromatics with reaction         conditions including a temperature of from about 275° C. to         about 600° C., a pressure of from about 0.5 atmosphere to about         50 atmospheres and a liquid hourly space velocity of from about         0.1 to about 100.     -   (V) The oligomerization of straight and branched chain olefins         having from about 2 to about 5 carbon atoms. The oligomers which         are the products of the process are medium to heavy olefins         which are useful for both fuels, i.e., gasoline or a gasoline         blending stock, and chemicals. The oligomerization process is         generally carried out by contacting the olefin feedstock in a         gaseous phase with a zeolite-bound high silica zeolite at a         temperature in the range of from about 250° C. to about 800° C.,         a LHSV of from about 0.2 to about 50 and a hydrocarbon partial         pressure of from about 0.1 to about 50 atmospheres. Temperatures         below about 250° C. may be used to oligomerize the feedstock         when the feedstock is in the liquid phase when contacting the         zeolite-bound high silica zeolite catalyst. Thus, when the         olefin feedstock contacts the catalyst in the liquid phase,         temperatures of from about 10° C. to about 250° C. can be used.     -   (W) The conversion of C₂ unsaturated hydrocarbons (ethylene         and/or acetylene) to aliphatic C₆₋₄₂ aldehydes and converting         said aldehydes to the corresponding C₆₋₄₂ alcohols, acids, or         esters.     -   (X) The desulfurization of FCC (fluid catalytic cracking) feed         streams. The desulfurization process is generally carried out at         a temperature ranging from 100° C. to about 600° C., preferably         from about 200° C. to about 500° C., and more preferably from         about 260° C. to about 400° C., at a pressure ranging from 0 to         about 2000 psig, preferably from about 60 to about 1000 psig,         and more preferably from about 60 to about 500 psig, at a LHSV         ranging from 1 to 10 h⁻¹. The hydrocarbon mixtures which can be         desulfurized according to the process of the present invention         contain more than 150 ppm of sulfur, e.g., hydrocarbon mixtures         with a sulfur content higher than 1000 ppm, even higher than         10000 ppm.

The invention having been generally described, the following examples are given as particular embodiments of the invention and to demonstrate the practice and advantages thereof. It is understood that the examples are given by way of illustration and are not intended to limit the specification or the claims to follow in any manner.

Example 1 Pt/Ge—Sn—Al-ZSM-5

Chemicals Used:

-   -   Ludox AS-40 colloidal silica SiO₂; 40 wt. % suspension in water;         Aldrich;     -   Sodium hydroxide NaOH, 50 wt. % solution in water;         Sigma-Aldrich;     -   Tin (II) chloride dihydrate 5 nCl₂.2H₂O, 98%; Sigma-Aldrich;     -   Germanium dioxide GeO₂; Germanium Corporation of America GTAH         68002;     -   Sodium aluminate NaAlO₂ (23.6 wt. % Al₂O₃; 19.4 wt. % Na₂O; 57.0         wt. % H₂O); Southern Ionics;     -   Tetrapropylammonium bromide (CH₃CH₂CH₂)₄NBr, TPABr; 98%;         Alfa-Aesar;     -   Acetic acid CH₃CO₂H, 99.7%; Aldrich.     -   Tetraammineplatinum nitrate (NH₂)₄Pt(NO₃)₂; >50.0% as Pt;         Aldrich.         Solutions:     -   Solution 1. 2.21 grams of tin chloride dihydrate were dissolved         in 55 grams of D.I. water. 25.98 grams of sodium hydroxide         solution were added with stirring. 7.11 grams of GeO2 were         dissolved in the solution.     -   Solution 2. 3.84 grams of sodium aluminate were homogenized in         50 grams of D.I. water.     -   Solution 3. 28.12 grams of TPABr were dissolved in 100 grams of         D.I. water.

Solution 1 was added to 150 grams of Ludox AS-40 with gel formation. Stirring was made for 10 minutes. Then solution 2 was introduced to gel. Gel was stirred for 15 minutes. Then solution 3 was added to gel and stirring was continued for 60 minutes.

15.97 grams of acetic acid were added gradually with gel stirring. Gel pH was measured in 15 minutes after acid addition (pH=9.78).

Crystallization was made in 1 L stainless steel autoclave at 160° C. for 113 hours with stirring (300 rpm).

Material was washed on filter with D.I. water, dried at 90° C., sieved 40 mesh size and calcined at 550° C. for 10 hours.

XRF analysis results are: 0.915 wt. % Na; 40.28 wt. % Si; 0.69 wt. % Al; 2.21 wt. % Sn; 5.80 wt. % Ge.

Ge—Sn-ZSM-5 zeolite was bound with silica at 50/50 wt. Bound zeolite was dried at 90° C. and calcined at 550° C. for 6 hours. Material was crushed and sieved 20/40 mesh size. Then ion-exchange with ammonium was made by sample treatment with 0.5M NH₄NO₃ at 60° C. in tree steps. Sample was rinsed with D.I. water, dried at 90° C. and calcined at 550° C. for 6 hours.

Platinum was introduced into catalyst by ion-exchange with 0.005M (NH₂)₄Pt(NO₃)₂ at 60° C. After rinsing with D.I. water catalyst was dried at 60° C. overnight and calcined in air at 300° C. for 3.5 hours.

XRF analysis results are: 0.079 wt. % Na; 45.11 wt. % Si; 0.39 wt. % Al; 1.11 wt. % Sn; 1.77 wt. % Ge; 0.35 wt. % Pt.

Example 2 Pt/Sn-ZSM-5 (no Al)

Chemicals Used:

-   -   Ludox AS-40 colloidal silica SiO₂; 40 wt. % suspension in water;         Aldrich;     -   Sodium hydroxide NaOH, 50 wt. % solution in water;         Sigma-Aldrich;     -   Tin (II) chloride dihydrate 5 nCl₂. 2H₂O, 98%; Sigma-Aldrich;     -   Tetrapropylammonium bromide (CH₃CH₂CH₂)₄NBr, TPABr; 98%;         Alfa-Aesar;     -   Acetic acid CH₃CO₂H, 99.7%; Aldrich.     -   Tetraammineplatinum nitrate (NH₂)₄Pt(NO₃)₂; >50.0% as Pt;         Aldrich.         Solutions:     -   Solution 1. 4.60 grams of tin chloride dihydrate were dissolved         in 105 grams of D.I. water. 25.97 grams of sodium hydroxide         solution were added with stirring.     -   Solution 2. 28.12 grams of TPABr were dissolved in 100 grams of         D.I. water.

Solution 1 was added to 150 grams of Ludox AS-40 with gel formation. Stirring was made for 30 minutes. Then Solution 2 was added to gel and stirring was continued for 100 minutes.

12.85 grams of acetic acid were added gradually with gel stirring. Gel pH was measured in 10 minutes after acid addition (pH=11.28). Crystallization was made in 1 L stainless steel autoclave at 160° C. for 96 hours with stirring (200 rpm). Material was washed on filter with D.I. water, dried at 90° C., sieved 40 mesh size and calcined at 550° C. for 10 hours.

XRF analysis results are: 0.894 wt. % Na; 42.97 wt. % Si; 5.13 wt. % Sn.

Sn-ZSM-5 zeolite was bound with silica at 50/50 wt. Bound zeolite was dried at 90° C. and calcined at 550° C. for 6 hours. Material was crushed and sieved 20/40 mesh size. Then ion-exchange with ammonium was made by sample treatment with 0.5M NH₄NO₃ at 60° C. in tree steps. Sample was rinsed with D.I. water, dried at 90° C. and calcined at 550° C. for 6 hours.

Platinum was introduced into catalyst by ion-exchange with 0.005M (NH₂)₄Pt(NO₃)₂ at 60° C. After rinsing with D.I. water catalyst was dried at 60° C. overnight and calcined in air at 300° C. for 4 hours.

XRF analysis results are: 0.073 wt. % Na; 45.36 wt. % Si; 2.49 wt. % Sn; 0.08 wt. % Pt.

Example 3 Pt/Sn—Al-ZSM-5

Chemicals Used:

-   -   Ludox AS-40 colloidal silica SiO₂; 40 wt. % suspension in water;         Aldrich;     -   Sodium hydroxide NaOH, 50 wt. % solution in water;         Sigma-Aldrich;     -   Tin (II) chloride dihydrate 5 nCl₂. 2H₂O, 98%; Sigma-Aldrich;     -   Sodium aluminate NaAlO₂ (23.6 wt. % Al₂O₃; 19.4 wt. % Na₂O; 57.0         wt. % H₂O); Southern Ionics;     -   Tetrapropylammonium bromide (CH₃CH₂CH₂)₄NBr, TPABr; 98%;         Alfa-Aesar;     -   Acetic acid CH₃CO₂H, 99.7%; Aldrich.     -   Tetraammineplatinum nitrate (NH₂)₄Pt(NO₃)₂; >50.0% as Pt;         Aldrich.         Solutions:     -   Solution 1. 4.60 grams of tin chloride dihydrate were dissolved         in 55 grams of D.I. water. 25.97 grams of sodium hydroxide         solution were added with stirring.     -   Solution 2. 3.84 grams of sodium aluminate were homogenized in         50 grams of D.I. water.     -   Solution 3. 28.12 grams of TPABr were dissolved in 100 grams of         D.I. water.

Solution 1 was added to 150 grams of Ludox AS-40 with gel formation. Stirring was made for 5 minutes. Then Solution 2 was added to gel and stirring was continued for 15 minutes. Then solution 3 was added to gel and stirring was continued for 60 minutes. 14.30 grams of acetic acid were added gradually with gel stirring. Gel pH was measured in 15 minutes after acid addition (pH=10.60). Crystallization was made in 1 L stainless steel autoclave at 160° C. for 104 hours with stirring (200 rpm).

Material was washed on filter with D.I. water, dried at 90° C., sieved 40 mesh size and calcined at 550° C. for 10 hours.

XRF analysis results are: 0.852 wt. % Na; 42.64 wt. % Si; 0.79 wt. % Al; 3.19 wt. % Sn.

Sn—Al-ZSM-5 zeolite was bound with silica at 50/50 wt. Bound zeolite was dried at 90° C. and calcined at 550° C. for 6 hours. Material was crushed and sieved 20/40 mesh size. Then ion-exchange with ammonium was made by sample treatment with 0.5M NH₄NO₃ at 60° C. in tree steps. Sample was rinsed with D.I. water, dried at 90° C. and calcined at 550° C. for 6 hours.

Platinum was introduced into catalyst by ion-exchange with 0.005M (NH₂)₄Pt(NO₃)₂ at 60° C. After rinsing with D.I. water catalyst was dried at 60° C. overnight and calcined in air at 300° C. for 4.5 hours.

XRF analysis results are: 0.000 wt. % Na; 44.86 wt. % Si; 0.36 wt. % Al; 2.50 wt. % Sn; 0.34 wt. % Pt.

Example 4 Pt/B-ZSM-5

Chemicals Used:

-   -   Boric acid H₃BO₃; 99.99%; Aldrich;     -   Sodium hydroxide NaOH; >98%; Aldrich;     -   Tetrapropylammonium bromide (CH₃CH₂CH₂)₄NBr, TPABr; 98%;         Alfa-Aesar;     -   Ludox HS-30 SiO₂, colloidal silica, 30% suspension in water;         Sigma-Aldrich.

2.88 grams of sodium hydroxide were dissolved in 230 grams of D.I water. Then 1.2 grams of boric acid and then 36.20 grams of tetrapropylammonium bromide were dissolved in the same solution with stirring. Light gel was formed after 44.0 grams of silica source Ludox HS-30 were introduced. Crystallization was made in 1 L stainless steel autoclave at 165° C. for 5 days with stirring (100 rpm).

Analysis results are: 42.7 wt. % Si; 0.411 wt. % B.

B-ZSM-5 zeolite was bound with silica at 50/50 wt. Bound zeolite was dried at 90° C. and calcined at 550° C. for 6 hours. Material was crushed and sieved 20/40 mesh size. Then ion-exchange with ammonium was made by sample treatment with 0.5M NH₄NO₃ at 60° C. in tree steps. Sample was rinsed with D.I. water, dried at 90° C. and calcined at 550° C. for 6 hours.

Platinum was introduced into catalyst by ion-exchange with 0.005M (NH₂)₄Pt(NO₃)₂ at 60° C. After rinsing with D.I. water catalyst was dried at 60° C. overnight and calcined in air at 300° C. for 2 hours.

Analysis results are: 0.000 wt. % Na; 46.22 wt. % Si; 0.20 wt. % B; 0.27 wt. % Pt.

Example 5 Pt/B—Al-ZSM-5

Chemicals Used:

-   -   Boric acid H3BO3; 99.99%; Aldrich;     -   Sodium hydroxide NaOH; >98%; Aldrich;     -   Sodium aluminate NaAlO₂ (23.6 wt. % Al₂O₃; 19.4 wt. % Na₂O; 57         wt. % H₂O); Southern Ionics.     -   Tetrapropylammonium bromide (CH₃CH₂CH₂)₄NBr, TPABr; 98%;         Alfa-Aesar;     -   Ludox HS-30 SiO₂, colloidal silica, 30% suspension in water;         Sigma-Aldrich.

3.79 grams of sodium hydroxide were dissolved in 345 grams of D.I. water. 1.8 grams of boric acid were dissolved in the same solution. Then sodium aluminate (1.36 grams) was added and then 54.3 grams of tetrapropylammonium bromide were dissolved in the same solution with stirring. Silica source Ludox HS-30 (66.0 grams) was introduced into the solution with gel formation. Gel was stirred for 10-15 minutes (pH=13.03). Crystallization was made in 1 L stainless steel autoclave at 165° C. for 5 days with stirring (100 rpm).

Analysis results are: 37.5 wt. % Si; 0.248 wt. % B; 0.97 wt. % Al.

B—Al-ZSM-5 zeolite was bound with silica at 50/50 wt. Bound zeolite was dried at 90° C. and calcined at 550° C. for 6 hours. Material was crushed and sieved 20/40 mesh size. Then ion-exchange with ammonium was made by sample treatment with 0.5M NH₄NO₃ at 60° C. in tree steps. Sample was rinsed with D.I. water, dried at 90° C. and calcined at 550° C. for 6 hours.

Platinum was introduced into catalyst by ion-exchange with 0.005M (NH₂)₄Pt(NO₃)₂ at 60° C. After rinsing with D.I. water catalyst was dried at 60° C. overnight and calcined in air at 300° C. for 2 hours.

Analysis results are: 0.000 wt. % Na; 46.00 wt. % Si; 0.49 wt. % Al; 0.22 wt. % B; 0.36 wt. % Pt.

Example 6 Pt/Fe—Al-ZSM-5

Chemicals Used:

-   -   Tetraethylorthosilicate (C₂H₄O)₄Si, TEOS; 99.9%; Alfa-Aesar;     -   Iron (III) nitrate Fe(NO₃)₃. 9H₂O; 98+%; Strem Chemicals;     -   Sulfuric acid H₂SO₄; 95-98%; Sigma-Aldrich;     -   Tetrapropylammonium bromide (CH₃CH₂CH₂)₄NBr, TPABr; 98%;         Alfa-Aesar;     -   Sodium hydroxide NaOH, 50 wt. % solution in water;         Sigma-Aldrich;     -   Aluminum sulfate octadecahydrate Al₂(SO₄)₃. 18 H₂O; 98%;         Sigma-Aldrich.         Solutions:     -   Solution 1. 120 grams of TEOS were introduced added to 175 grams         if D.I. water and stirring was made to homogenize the solution.         1 gram of iron nitrate was dissolved in solution. 9.6 grams of         sulfuric acid were introduced gradually with stirring.     -   Solution 2. 14.4 grams of tetrapropylammonium bromide were         dissolved in 45 grams of D.I. water. 2 grams of sodium hydroxide         were added and then 6.93 grams of aluminum sulfate         octadecahydrate were dissolved on the solution.

Solution 2 was added to Solution 1 with stirring. pH was adjusted to 9 by addition of sodium hydroxide solution (about 22-23 grams). Viscous gel was formed. Crystallization was done in autoclave at 150° C. for 3 days with stirring (100 rpm).

Analysis results are: 1.252 wt. % Na; 44.65 wt. % Si; 1.87 wt. % Al; 0.45 wt. % Fe.

Fe—Al-ZSM-5 zeolite was bound with silica at 50/50 wt. Bound zeolite was dried at 90° C. and calcined at 550° C. for 6 hours. Material was crushed and sieved 20/40 mesh size. Platinum was introduced into catalyst by ion-exchange with 0.005M (NH₂)₄Pt(NO₃)₂ at 60° C. After rinsing with D.I. water catalyst was dried and calcined in air at 300° C.

Analysis results are: 0.533 wt. % Na; 44.39 wt. % Si; 0.97 wt. % Al; 0.23 wt. % Fe; 0.37 wt. % Pt.

Example 7 Pt/Ti—Al-ZSM-5

Chemicals Used:

-   -   Tetraethylorthosilicate (C₂H₄O)₄Si, TEOS; 99.9%; Alfa-Aesar;     -   Hydrochloric acid HCl 0.2N in water; Aldrich;     -   Isopropyl alcohol C₃H₈O; 99.7%; Alfa-Aesar;     -   Aluminum isopropoxide Al[OCH(CH₃)₂]₃; 97%; Fluka;     -   Tetrapropylammonium hydroxide (CH₃CH₂CH₂)₄NOH, TPAOH; 40%         solution in water; SACHEM;     -   Titanium tetrabutoxide Ti(OC₄H₉)₄; 97%; Aldrich.         Solutions:     -   Solution 1. Mixture of 24 grams of tetraethylorthosilicate and         15 grams of hydrochloric acid were stirred for 45 minuted.     -   Solution 2. 7.5 grams of isopropyl alcohol and 0.294 gram of         aluminum isopropoxide were mixed overnight.     -   Solution 3. 4 grams of TPAOH were mixed with 4 grams of D.I.         water.     -   Solution 4. 0.981 gram of titanium tetrabutoxide was homogenized         with 6 grams of isopropyl alcohol.

Solution 2 was added to Solution 1 by drops. Mixing was done for 45 minutes. Then 2.25 grams of Solution 3 were added and stirring was made at 0° C. for 15 minutes.

Solution 4 was introduced gradually into mixture at 0° C. and stirring was continued for an additional 20 minutes.

5.7 grams of Solution 3 was added slowly to the mixture and stirring was done at RT. Gel was formed. Gel was dried overnight at 110° C. Solid material was grinded to powder. Incipient wetness impregnation was used to impregnate the powder with 13.8 grams of Solution 3. Crystallization was made at 170° C. for 24 hours in 300 ml teflon lined autoclave in static regime. Crystalline product was centrifuged and washed with D.I. water. The product was dried at 110° C. overnight and calcined at 550° C. for 5 hours.

XRF analysis results are: 43.69 wt. % Si; 0.93 wt. % Al; 0.96 wt. % Ti.

Ti—Al-ZSM-5 zeolite was bound with silica at 50/50 wt. Bound zeolite was dried at 90° C. and calcined at 550° C. for 6 hours. Material was crushed and sieved 20/40 mesh size. Then ion-exchange with ammonium was made by sample treatment with 0.5M NH₄NO₃ at 60° C. in tree steps. Sample was rinsed with D.I. water, dried at 90° C. and calcined at 550° C. for 6 hours.

Platinum was introduced into catalyst by ion-exchange with 0.005M (NH₂)₄Pt(NO₃)₂ at 60° C. After rinsing with D.I. water catalyst was dried at 60° C. overnight and calcined in air at 300° C. for 2 hours.

Analysis results are: 0.000 wt. % Na; 45.42 wt. % Si; 0.43 wt. % Al; 0.44 wt. % Ti; 0.35 wt. % Pt.

All catalysts were reduced in a flowing hydrogen/nitrogen (50/50 by volume) mixture at 400° C. All catalysts were tested in a stainless steel tube at 500° C. using 34 cc/min propane at 22 psig total pressure. The products were analyzed by on-line sampling to a gas chromatograph where all hydrocarbon components with carbon numbers between 1 and 10 were quantitatively determined. Results for yield [fraction of BTX (benzene, toluene, xylenes) in product] and conversion (portion of propane converted) are shown in FIGS. 1-7.

Numerous modifications and variations of the present invention are possible in light of the above teachings. It is to be understood that, within the scope of the appended claims, the invention may be practiced other than as specifically described. 

What is claimed as new and desired to be secured by Letter of Patent of the United States of America is:
 1. A process for synthesizing a zeolite comprising: preparing a zeolite having incorporated into the zeolite framework germanium, titanium, tin, and aluminum in the zeolite framework; calcining the zeolite, said calcining occurring after preparation of the zeolite; depositing a metal selected from Group 6, Group 7, Group 8, Group 9, and Group 10, and combinations thereof, wherein the metal is only present as a deposited metal; wherein the zeolite is a MFI, MWW (MCM-22), LTL (Zeolite L), MTT (ZSM-23), MTW (ZSM-12), or MEL (ZSM-11) zeolite.
 2. A process for synthesizing a zeolite comprising: preparing a zeolite having incorporated into the zeolite framework germanium, titanium, and aluminum; and calcining the zeolite, said calcining occurring after preparation of the zeolite; depositing a metal selected from Group 6, Group 7, Group 8, Group 9, and Group 10, and combinations thereof, wherein the metal is only present as a deposited metal; wherein the zeolite is a MFI, MWW (MCM-22), MTT (ZSM-23), MTW (ZSM-12), or MEL (ZSM-11) zeolite.
 3. The process of claim 2, wherein the zeolite is MEL or MFI.
 4. The process of claim 2, further comprising depositing a metal selected from Group 10 on the zeolite.
 5. The process of claim 4, wherein the Group 10 metal comprises platinum.
 6. The process of claim 2, further comprising, in the zeolite framework, at least one of tin and boron.
 7. The process of claim 2, further comprising boron in the zeolite framework.
 8. A process for synthesizing a zeolite comprising: preparing a zeolite having incorporated into the zeolite framework germanium, aluminum, and titanium, wherein the zeolite comprises 0.63 and 0.96 weight percent germanium; and calcining the zeolite, said calcining occurring after preparation of the zeolite; depositing a metal selected from Group 6, Group 7, Group 8, Group 9, and Group 10, and combinations thereof, wherein the metal is only present as a deposited metal; wherein the zeolite is an MFI (ZSM-5), MWW (MCM-22), MTT (ZSM-23), MTW (ZSM-12), or MEL (ZSM-11) zeolite.
 9. The process of claim 3, wherein the zeolite is MEL or MFI.
 10. The process of claim 9, wherein the zeolite is MFI. 